ABS Valves are a pressure piping system that is both strong and rigid. ABS piping is a low-cost option for both commercial and residential applications.
It’s a great option for get-togethers. Acrylonitrile Butadiene Styrene (ABS) is an amorphous, impact-resistant, opaque thermoplastic commonly utilised in the plastics industry.
We are able to provide ABS Valve to our clients because of our extensive experience in this field The thermoplastic is composed out of three monomer units, as the name suggests:
When compared to other popular polymers, ABS has superior mechanical characteristics such as impact resistance, toughness, and stiffness.
To increase impact resistance, toughness, and heat resistance, several changes can be performed.
Increase the quantities of polybutadiene in ratio to styrene and also acrylonitrile to increase impact resistance, but this alters other characteristics. At lower temperatures, impact resistance does not deteriorate as quickly.
With restricted loads, the stability under load is excellent. ABS Valve and Pipe Fittings are very easy installation and reliable for used.
Density | |
---|---|
Test method | ISO 1183 – ASTM D792 |
Unit of measurement | g/cm3 |
Value | 1.38 |
Modulus of elasticity | |
Test method | ISO 527 |
Unit of measurement | MPa = N/mm2 |
Value | 3200 |
IZOD notched impact strength at 23°C | |
Test method | ASTM D256 |
Unit of measurement | J/m |
Value | 50 |
Ultimate elongatio | |
Test method | ISO 527 |
Unit of measurement | % |
Value | 50 |
Shore hardness | |
Test method | ISO 868 |
Unit of measurement | Shore D |
Value | 80 |
Tensile strength | |
Test method | ISO 527 |
Unit of measurement | MPa = N/mm2 |
Value | 50 |
VICAT softening point (B/50) | |
Test method | ISO 306 |
Unit of measurement | °C |
Value | 76 |
Heat distortion temperature HDT (0.46 N/mm2) | |
Test method | ASTM D648 |
Unit of measurement | °C |
Value | 86 |
Thermal conductivity at 23° C | |
Test method | DIN 52612-1 – ASTM C177 |
Unit of measurement | W/(m °C) |
Value | 0.16 |
Coefficient of linear thermal expansion | |
Test method | DIN 53752 – ASTM D696 |
Unit of measurement | m/(m °C) |
Value | 8 x 10-5 |
Limiting Oxygen Index | |
Test method | ISO 4859-1 – ASTM D2863 |
Unit of measurement | % |
Value | 45 |
Production of the PVC-U lines is carried out according to the highest quality standards and in full compliance with the environmental restrictions set by the applicable laws in force and in accordance with ISO 14001. All products are made in accordance with the quality guarantee system in compliance with ISO 9001.
• ANSI B16.5 |
Pipe flanges and flanged fittings-NPS 1/2 to NPS 24 mm / inch |
• ASTM D 2464 |
Standard Specification for Threaded Poly Vinyl Chloride (PVC) Plastic Pipe |
Fittings |
• ASTM D 2467 |
Standard Specification for Poly Vinyl Chloride (PVC) Plastic Pipe Fittings, |
Schedule 80 |
• BS 10 |
Specification for flanges and bolts for pipes, valves and fittings |
• BS 1560 |
Flanges for pipes, valves and fittings (Class designated). Steel, cast iron |
and copper alloy flanges. Specification for steel flanges |
• BS 4504 |
Flanges for pipes, valves and fittings (PN designated). |
• DIN 2501 |
Flanges, dimensions |
• DIN 2999 |
Whitworth thread for threaded pipes and fittings |
• DIN 3202 |
Overall valve dimensions |
• DIN 3441-2 |
Dimensions of PVC-U ball valves |
• DIN 8062 |
Dimensions of PVC-U pipes |
• DIN 8063 |
Dimensions of PVC-U fittings |
• DIN 16962 |
PVC-C fittings for butt-welding or socket fusion, dimensions |
• DIN 16963 |
Pipe connections and pipe components for pressurised fluids in HDPE |
• DVS 2204 – 2221 |
Solvent welding of thermoplastic materials PVC-U |
• EN 558-1 |
Industrial valves – face-to-face and centre-to-face dimensions of metal |
valves for use in flanged pipe systems – Part 1: PN designated valves |
• EN 1092-1 |
Flanges and their joints – Circular flanges for pipes, valves and accessories |
– Part 1: Steel flanges, PN designated |
• EN ISO 1452 |
Characteristics of fittings and pipes in PVC-U for piping systems intended |
for water supply |
Solvent welding, or cement jointing, is the longitudinal joining system for connecting rigid PVC-U pipes and fittings. The “cementing” is carried out using adhesives/cements obtained by dissolving PVC-U polymer in a solvent mixture. This solvent liquefies the walls of the pipe and/or fitting, allowing the constituent material to chemically combine and be subse-quently welded. Chemical welding allows permanent joints be achieved possessing
chemical and mechanical strength characteristics identical to those of the pipes and fittings joined. The adhesives/solvent cements must be selected according to the type of thermoplastic resin to weld, in that the nature of the solvents vary, as does
the weld material contained in them. It must be remembered, therefore, that all the solvent cements designed for joining thermoplastic pipes and fittings must be used to join pipes, fittings and valves of the same material.
Before starting any solvent welding operations, the efficiency and condition of the equipment used and the pieces to be assembled must be verified, in particular the uniformity, fluidity and expiry date of the solvent cement.
Cut the pipe perpendicular to its axis to obtain a clean square section, preferably using a wheeled pipe cutter designed specifically for thermoplastic pipes (fig. 1).
Fig 1
Chamfer the outer edges of the pipe in order to ensure that it enters the socket of the fitting at an angle of 15°. The chamfering operation must be carried out at all costs, otherwise the lack of chamfer can lead to the solvent being scraped off the surface of the fitting, thus compromising the effectiveness of the joint. The chamfering must be carried out using the appropriate chamfering tool (fig. 2).
Fig 2
Measure the depth of the socket of the fitting to the internal shoulder and mark the corresponding distance on the end of the pipe (fig. 3 and 4). For more de- tails, refer to the “Socket depth, cement and chamfer length” table.
Fig 3
Fig 4
Using an clean paper towel or applicator soaked in Cleaner-Primer, remove any traces of dirt or grease from the outer surface of the pipe for the entire cement-ing length. Repeat the same operation on the internal surface of the socket of the fitting: leaving the surfaces softened (fig. 5).
Leave the surfaces to dry for a few minutes before applying the solvent cement. Remember that, in addition to cleaning the joint surfaces, the Cleaner-Primer also performs the important role of softening and preparing the surface to receive the solvent, an operation that enables a perfect joint to be obtained.
Fig 5
Apply the solvent cement in a uniform manner longitudinally over both parts to be assembled (outer surface of the pipe and internal coupling surface of the fit-ting) using an applicator or suitably sized coarse brush.
For more detailed information, refer to the “Brush-applicator characteristics and dimensions” table. It is advisable to use an applicator/brush of dimension not less than half the di-ameter of the pipe. The solvent cement must be applied along the entire length
of the joining surface of both the pipe and the fitting:
– for the entire joint length of the pipe previously marked on the outer surface
(fig. 6)
– for the entire depth of the socket as far as the internal shoulder (fig.7)
Fig 6
Fig 7
Fully insert the pipe into the fitting immediately and without any rotation. Only after this operation will it be possible to slightly rotate both ends (max. 1/4 of a turn between pipe and fitting). This rotation movement will render the layer of applied solvent cement more uniform (fig. 8)
Fig 8
The pipe must be inserted in the fitting as soon and as quick as possible (after no more than 20-25 seconds is recommended). Depending on the external diameter of the pipe and, as a result, possible handling difficulties, the insertion of the pipe
into the fitting must be carried out:
– manually by one person for external diameters < 90 mm.
– manually by two people for external diameters from d 90 to d < 160 mm. – using mechanical pipe-pullers for external diameters > 160 mm.
Immediately after fully inserting the pipe in the fitting, apply pressure to the joined parts for a few seconds. Then use crepe paper or a clean cloth to remove any excess solvent cement from the outer surfaces, and from internal surfaces where possible (fig. 9).
Fig 9
Solvent cement drying: the joined parts must be left to stand in order to allow the solvent cement to set naturally without generating any unnecessary stress. The setting time depends on the amount of stress that the joint will be placed under.
In particular, the following minimum setting times must be respected according
to the ambient temperature:
• before handling the joint:
– from 5 to 10 minutes for ambient T. > 10°C
– from 15 to 20 minutes for ambient T. < 10°C
• for repair joints on pipes of any size or pressure not subject to hydraulic testing:
– 1 hour for each atm of applied pressure
• for joints in pipes and fittings of any diameter subject to pressure testing up to
PN 16:
– minimum 24 hours
The solvent cement setting times indicated are valid at ambient temperature
(approx. 25°C.). For particular climatic conditions (humidity, temperature, etc…),
we recommend you contact our technical services department and/or the solvent
cement manufacturer for more information (fig. 10 and 11).
Fig 10
Fig 11